TYPE K THERMOCOUPLE (Chromel / Alumel)
Tweet
Composed of a positive leg, which is approximately 90% nickel, 10 chromium and a negative leg, which is approximately 95% nickel, 2% aluminum, 2% manganese and 1% silicon.
Due to its reliability and accuracy, Type K is used extensively at temperatures up to 1260°C (2300°F). It's good practice to protect this type of thermocouple with a suitable metal or ceramic protecting tube, especially in reducing atmospheres. In oxidizing atmospheres, such as electric furnaces, tube protection is not always necessary when other conditions are suitable; however, it is recommended for cleanliness and general mechanical protection. Type K will generally outlast Type J because the JP (iron) wire rapidly oxidizes, especially at higher temperatures.
Type K (chromel{90 percent nickel and 10 percent chromium}–alumel)(Alumel consisting of 95% nickel, 2% manganese, 2% aluminium and 1% silicon) is the most common general purpose thermocouple with a sensitivity of approximately 41 µV/°C, chromel positive relative to alumel. It is inexpensive, and a wide variety of probes are available in its −200 °C to +1350 °C / -328 °F to +2462 °F range. Type K was specified at a time when metallurgy was less advanced than it is today, and consequently characteristics vary considerably between samples. One of the constituent metals, nickel, is magnetic; a characteristic of thermocouples made with magnetic material is that they undergo a step change in output when the magnetic material reaches its Curie Point (around 354 °C for type K thermocouples).